Mg2MM&#39;o 6+x, (M=Y, rare earth metal and M&#39;=Sn, OR Zr) dielectric ceramics

ABSTRACT

This invention relates to a new group of complex ceramic oxides and a process for their production. This group of novel complex ceramic oxides are of the general formula Mg 2 MM′O 6+x , where M=Rare Earth metal ion or Yttrium or Lanthanum and M′=Sn, Sb, Zr, Hf, Ta, and Nb; and where −0.5&lt;x&lt;+0.5; and have a defective pyrochlore structure. Minor variations in the compositions up to 8% in any of the metal ions may be tolerated for the formation of the required phase. The process for the preparation of the novel class of compounds comprises: (a) Mixing the compounds of magnesium, M and M′ (where M may be Yttrium, Lanthanum or any of the Rare Earth metals; and M′=Antimony, Tin, Zirconium or tantalum) in such a way as to get the molar ratio of Mg:M:M′ as 2:1:1 required for the formation of the compounds of the general formula Mg2MM′O6+x. Minor variations in the compositions up to 8% in one metal ions may be tolerated for the formation of the required phase. (b) The compounds employed in step (i) may be selected from their oxides, carbonates, chlorides, alkoxides, nitrates, sulfates etc.; preferably the salts used are selected from oxides or carbonates. (c) The mixture obtained in step (i) may be ball milled or mixed with a wetting medium. The wetting medium may be water, alcohol, acetone or any other organic solvent. The resultant ball milled slurry may be dried to remove the liquid and obtain dry powder, (d) Heating the resultant mixture to a temperature in the range 1000-1600° C., as required for different duration ranging from 3 hours to 50 hours, either in a single step or by taking out the reactant after few hours of heating, checking for phase formation and heating it again after grinding, if necessary. Up to a maximum of 5 intermediate grindings may be required.

This invention relates to a new group of complex ceramic oxides and a process for their production. This invention particularly relates to novel complex ceramic oxides of the general formula Mg₂MM′O_(6+x), where M=rare earth metal ion or Y and M′=Sn, Sb, Zr, Hf, Ta, and Nb; having a defect pyrochlore structure and the solid state reaction method of their preparation. The complex ceramic powders of the present invention are useful for active and passive electronic applications, for temperature stable, low loss, high permitivity dielectric applications, for temperature stable and temperature compensating dielectrics; microwave dielectrics and as co-fired microwave components, for electrodes of Fuel cells, as catalyst (solid photocatalysts, oxidation catalysts), as gas monitoring sensors, as possible host for radioactive wastes and as host for fluorescence centers.

Introduction

In recent years, there has been a raising order of interest in the preparation and characterization of complex ceramic oxides, with the general formula A₂MM′O_(6+x); where A=Ba, Sr and Ca; M=Y and rare earths and M′=Sb, Sn, Nb, Zr, Hf and Ta. The compounds with general formula Ba₂MM′O_(6+x) crystallize in the perovskite structure. Some of the compounds with the formula Sr₂MM′O_(6+x), are also reported. They also possess the perovskite structure. Some of the compounds reported in these system are; Sr₂GaNbO₆, Sr₂GaTaO₆, Sr₂AlNbO₆, Sr₂AlTaO₆, Ca₂GaNbO₆, Ca₂GaTaO₆, Ca₂AlNbO₆, Ca₂AlTaO₆, Ba₂DySnO_(5.5), Ba₂EuNbO₆, Ba₂ErSbO₆, YBa₂NbO₆, Ba₂DySbO₆ Ba₂PrHfO_(5.5) (J Koshy, K S Kumar, J Kurian Y P Yadava and A D Damodaran; Rare-earth barium Stannates Synthesis, characterization and potential use as substrate for YBa₂Cu₃O_(7-n); Journal of American Ceramic Society; 78[11]5088-92 (1995)., and C D Bradle and V J Fratello; preparation of perovskite oxides for high Tc superconductor substrates; Journal of Materials. Research, volume-5, Number-10 pages 2160-2164 year 1990). These compounds were prepared by the conventional solid state reaction technique or by using an exothermic combustion of a polymeric precursor at a relatively low temperature. (J Koshy, J Kurian, R Jose, A M John, P K Sajith, J James, S P Pai and R Pinto; Bulletin of Material Science, Volume-22, Number-3 May 1999 pages243-249; A M John, R Jose and J Koshy; Synthesis and rapid densification of nanoparticles of Barium Praseodymium Hafnium Oxide: a complex perovskite; Journal of Nanoparticle research, volume-3 year 2001 pages-413-417). However in case of Ca₂MM′O_(6+x) compounds apart from the perovskite structure, a few cases of meta stable pyrochlore structures were also reported. These meta stable pyrochlores transformed into perovskite structures at about 650-700° C. (J Koshy, J Kurian, R Jose, Asha M John, P K Sajith, J James, S P Pai and R Pinto “Novel ceramic substrate for high Tc superconductors” Bulletin of Material Science, vol.22, pp243-249 (1999); S Ya Istomin, O G D'yachenko and E V Antipov, Synthesis and characterization of reduced niobates CaLnNb₂O₇. Ln=Y, Nd with pyrochlore structure; Materials Research Bulletin, vol.32, No.4, pp 421-30, (1997); J Koshy, J Kurian, P K Sajith, K S Kumar, R Jose, Asha M John and A D Damodaran; Novel ceramic substrate for Bi-cuperate superconductors; U.S. Pat. No. 5,741,747 dated Apr. 21, (1998)). Some of the magnesium bearing ceramic oxides reported for possible use in electronic ceramic applications are Sr₂MgMoO₆, La₂MgTiO₆, Gd₂MgTiO₆, Gd₂MgZrO₆ and La₂MgGeO₆, (C D Bradle and V J Fratello, preparation of perovskite oxides for high Tc superconductor substrates: Journal of Materials Research, volume-5, Number-10 pages-2160-2164 year 1990). Most of the above mentioned compounds had a perovskite structure. However some of the Magnesium bearing compounds that were reported are Ba(Mg_(1/3)Ta_(2/3))O₃ and PbMg_(1/3)Nb_(2/3)O₃ and Bi₂M′_(2/3)M″_(4/3)O₇ where M′=Zn, Mg, Ni, Sc, In and Cu and M″=Nb and Ta (M Valant and P K Davis; Synthesis and dielectric properties of pyrochlore solid solutions in the Bi₂O₃—ZnO—Nb₂O₅—TiO₂ system. Journal of Material Science 34(1999) 5437-5442). Some of these magnesium-bearing compounds had pyrochlore structures, However compounds of the type Mg₂MM′O_(6+x) either with perovskite structure or pyrochlore structure were not reported.

Pyrochlore structures are the structures with the general formula A₂B₂O₇, where A atoms are 8 coordinated and B atoms are 6 coordinated with one extra O-atom. In recent years many pyrochlore compounds with more complicated composition (AA′)₂(BB′)₂O₇ have been synthesized. For the possibility of existence of any pyrochlore compound, there are two criteria: (1) the ratio of the ionic radius of the cation at the A site to that at the B site must be between 1.46 and 1.80 and (2) the chemical valencies of the various ions must make the compound neutral. (Y Xuan, R Liu and Y Q Jia; Synthesis of a new series of compounds RE₂Co_(2/3)Nb_(4/3)O₇ and stability field diagram of RE₂B_(2/3)′B_(4/3)″O₇ pyrochlore compounds; Materials Chemistry and Physics, vol-53, pp256-261 (1998)). Pyrochlore compounds have been extensively studied over the past because of their specific properties and consequent technological applications. Some of the very important properties of members of this group of compounds are: low thermal conductivity, high melting point, high thermal expansion coefficient, high stability. They can be used in Gas turbines and diesel engines as thermal barrier coatings. Some of the pyrochlore compounds exhibit high ionic conductivity and can be used as electrodes for Fuel cells, egs, Gd₂TiMoO_(7+x); Gd₂TiO_(7+x) (P Holtappels, F W Poulsen and M-Mogensen; Electrical conductivities and chemical stabilities of mixed conducting pyrochlores for Solid oxide fuel cell applications; Solid State Ionics, vol.135, pp675-679 (2000)). Pyrochlore oxides also exhibit catalytic properties and are used as solid photocatalysts (eg. Bi₂MNbO₇, M-Al, Ga, In) (Zhigang Zou, Jinhua Ye and Hironori Arakawa, Preparation, structural and optical properties of a new class of compounds, Bi₂MNbO₇ (M=Al, Ga, In); Materials Science and Engineering vol. B79, pp83-85 (2001)), oxidation catalysts and as gas monitoring sensors. They have the ability to accommodate defects and act as possible host for radioactive wastes, and as host for fluorescence centers. Some of the pyrochlore materials also show superconductivity and magnetic properties, including Colossal Magneto resistant behavior; e.g. Sm₂Ti₂O₇, La₂Zr₂O₇, Nd₂Zr₂O₇, La_(0.7)Ba_(0.3)MnO₃, (L Li, Y W Song, H Xiong, Y Q Jia, N Matsushita and Y Xuan; Synthesis, crystal structure and magnetic properties of Sm_(2-x)Co_(x)Ti_(2-y)Nb_(y)O₇ (x=0, 0.2, 0.4); Materials Chemistry and Physics, vol-9273, pp. 1-7 (2002); K Koteswara Rao, Taqveem Banu, M Vital, G Y S K Swamy and K Ravi Kumar, Preparation and characterization of bulk and nanoparticles of La₂Zr₂O₇ and Nd₂Zr₂O₇ by sol-gel method; Materials letters; vol.54, pp.205-210 (2002))

Pyrochlores have been used in active and passive electronic applications. They are recently recognized as potential candidates for temperature stable, low loss, high permitivity dielectric applications and in temperature stable and temperature compensating dielectrics; microwave dielectrics and as co-fired microwave components (P Holtappels, F W Poulsen and M Mogensen; Electrical conductivities and chemical stabilities of mixed conducting pyrochlores for SOFC applications; Solid State Ionics, vol.135, pp675-679 (2000)).

However no compound of the formula Mg₂MM′O_(6-x) (where −0.5<x<+0.5 and M=Yttrium or Lanthanum or any of the Rare Earth metal ions; and M′=Sb, Sn, Zr, & Ta) has been reported till now.

Objectives

The main objective of the present invention is to provide a novel Magnesium based class of complex ceramic oxides, that could be used (i) for active and passive electronic applications, (ii) for temperature stable, low loss, high permitivity dielectric applications (iii) for temperature stable and temperature compensating dielectrics; microwave dielectrics and as co-fired microwave components (iv) for electrodes for Fuel cells (v) as catalyst (solid photocatalysts, oxidation catalysts) (vi) as gas monitoring sensors. (vii) as possible host for radioactive wastes, and (iii) as host for fluorescence centers.

Another objective of the present invention is to prepare a novel class of complex ceramic oxides having the formula Mg₂MM′O_(6+x) where M=Y, La and rare earth metal ions; and M′=Sb, Sn, Zr, and Ta and having a defect pyrochlore structure.

Yet another objective of the present invention is to provide a method for the preparation of a novel magnesium bearing class of complex ceramic oxides having the above formula, structure and uses.

Invention

We have now prepared a new class of Mg bearing compounds with the general formula Mg₂MM′O_(6+x), (M=Y, La and rare earth metal ions; and M′=Sb, Sn, Zr, and Ta)-having a defect pyrochlore structures. Accordingly the invention provides a process for the preparation of the above mentioned class of compounds which comprises:

-   (i) Mixing the compounds of magnesium, M and M′ (where M may be     Yttrium, or any of the rare earth metals; and M′=Antimony, Tin,     Zirconium or tantalum) in such a way as to get the molar ratio of     Mg:M:M′ as 2:1:1 required for the formation of the compounds of the     general formula Mg₂MM′O_(6+x). Minor variations in the compositions     up to 8% in one metal ions may be tolerated for the formation of the     required phase. -   (ii) The compounds employed in step (i) may be selected from their     oxides, carbonates, chlorides, alkoxides, nitrates, sulphates etc.;     preferably the salts used are selected from oxides or carbonates. -   (iii) The mixture obtained in step (i) may be ball milled or mixed     with a wetting medium. The wetting medium may be water, alcohol,     acetone or any other organic solvent. The resultant ball milled     slurry may be dried to remove the liquid and obtain dry powder. -   (iv) Heating the resultant mixture to a temperature in the range     1000-1450° C. as required for different duration ranging from 3 hour     to 50 hours, either in a single step or by taking out the reactant     after few hours of heating, checking for phase formation and heating     it again after grinding if necessary. Up to a maximum of 5     intermediate grindings may be required.

The complex ceramic powders of the present invention are useful (i) for active and passive electronic applications, (ii) for temperature stable, low loss, high permitivity dielectric applications (iii) for temperature stable and temperature compensating dielectrics; microwave dielectrics and as co-fired microwave components (iv) for electrodes for Fuel cells (v) as catalyst (solid photocatalysts, oxidation catalysts) (vi) as gas monitoring sensors. (vii) as possible host for radioactive wastes, and (iii) as host for fluorescence centers.

The details of the present invention are described in the examples given below. These examples are provided by way of illustration only and should not be construed to limit the scope of the invention.

Accordingly, the present invention provides novel compounds of the general formula Mg₂MM′O_(6-x) where M=Y, La or a rare earth metal, M′=Sn, Sb, Zr and Ta, 0.5<x<0.5 having pyrochlore structure, wherein minor variations in the compositions up to 8%, in any of the metal ions is tolerated for the formation of the required phase, and, a process for the preparation of the said novel compounds comprising:

-   (i) Mixing the compounds of magnesium, M and M′ (where M=Y, La or a     rare earth metal. M′=Sn, Sb, Zr and Ta) in such a way as to get the     molar ratio of Mg:M:M′ as 2:1:1 required for the formation of the     compounds of the general formula Mg₂MM′O_(6+x), wherein minor     variations in the compositions up to 8% in any of metal ion is     tolerated for the formation of the required phase; -   (ii) the mixture obtained in step (i) is ball milled or mixed with a     wetting medium; -   (iii) the resultant ball milled slurry obtained is dried to remove     the liquid and obtain dry powder: -   (iv) Heating the resultant mixture to a temperature in the range     1000-1600° C. as required for different duration ranging from 3 hour     to 50 hours, either in a single step or by taking out the reactant     after few hours of heating, checking for phase formation and heating     it again after grinding if necessary, upto a maximum of 5     intermediate grindings may be required.

In an embodiment of the present invention, the compounds employed in the process are selected from their oxides, carbonates chlorides, alkoxides, nitrates, sulfates etc. and preferably the salts used are selected from oxides or carbonate.

In another embodiment of the present invention the wetting medium used in the process is selected from water, alcohol, acetone or any other organic solvent.

In another embodiment of the present invention, novel compound obtained is of the formula Mg₂SmTaO₆ as nanoparticle having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated For the formation of the phase.

In still another embodiment of the present invention, novel compound obtained is of the formula Mg₂NdTaO₆ as nanoparticle having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.

In yet another embodiment of the present invention, novel compound obtained is of the formula Mg₂DyTaO₆ as nanoparticle having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.

In yet another embodiment of the present invention, novel compound obtained is of the formula Mg₂PrTaO₆ as nanoparticle having pyrochlore structure wherein for the formation of the phase.

In yet another embodiment of the present invention, novel compound obtained is of the formula Mg₂GdTaO₆ as nanoparticle having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.

In still another embodiment of the present invention, novel compound obtained is of the formula Mg₂EuTaO₆ as nanoparticle having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.

In still another embodiment of the present invention, novel compound obtained is of the formula Mg₂LaTaO₆ as nanoparticle having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.

In further embodiment of the present invention, novel compound obtained is of the formula Mg₂DySbO₆ as nanoparticle having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.

In further embodiment of the present invention, novel compound obtained is of the formula Mg₂SmZrO_(5.5) as nanoparticle having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.

In still further embodiment of the present invention, novel compound obtained is of the formula Mg₂NdZrO_(5.5) as nanoparticle having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.

In still embodiment of the present invention, novel compound obtained is of the formula Mg₂DyZrO_(5.5) as nanoparticle having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.

In yet further embodiment of the present invention, novel compound obtained is of the formula Mg₂LaSnO_(5.5) as nanoparticle having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.

In yet further embodiment of the present invention, novel compound obtained is of the formula Mg₂GdZrO_(5.5) as nanoparticle having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.

In still another embodiment of the present invention, novel compound obtained is of the formula Mg₂EuZrO_(5.5) as nanoparticle having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.

In yet another embodiment of the present invention, novel compound obtained is of the formula Mg₂LaZrO_(5.5) as nanoparticle having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.

In still further embodiment of the present invention, novel compound obtained is of the formula Mg₂PrZrO_(5.5) as nanoparticle having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.

EXAMPLE-1 Magnesium Samarium Tantalate (Mg₂SmTaO₆)

Magnesium Samarium Tantalate (Mg₂SmTaO₆), for example, is obtained by;

-   -   (i) Taking four gram molecular weight of Magnesium Carbonate         (MgCO₃), one gram molecular weight of Samarium Oxide (Sm₂O₃),         and one gram molecular weight of Tantalum oxide (Ta₂O₅)     -   (ii) Mixing these three reactants by ball milling the mixture         for 24 hours using water as the wetting medium.     -   (iii) Drying the ball milled reaction mixture (sample) in an         oven at about 120° C.     -   (iv) Pelletizing the sample and heating at 1400° C. for 10 hours         with three intermediate grinding.     -   (v) The XRD pattern of this compound is shown in FIG. 1.     -   (vi) Considering the highest possible oxidation states of the         metals used; (Mg—+2, Sm—+3 and Ta—+5) the chemical formula of         the compound Magnesium Samarium Tantalate is worked out to be         Mg₂SmTaO₆.     -   (vii) The variation of dielectric constant and loss factor of         the compound Mg₂SmTaO₆ is shown in FIG. 2 and FIG. 3. This         clearly shows that the compound is suitable for use as         electronic ceramic material for all applications where the         dielectric constant plays a crucial role. E.g. substrate for         superconductors.     -   (viii) The compound does not show any phase transition on         heating up to 1300° C.

EXAMPLE-2 Magnesium Lanthanum Stanate (Mg₂LaSnO_(5.5))

Magnesium Lanthanum Stanate (Mg₂LaSnO_(5.5)), for example, is obtained by;

-   -   (i) Taking four gram molecular weight of Magnesium Carbonate         (MgCO₃), one gram molecular weight of lantanum oxide (La₂O₃),         and one gram molecular weight of Tin oxide (SnO₂)     -   (ii) Mixing these three reactants by ball milling the mixture         for 12 hours using water as the wetting medium.     -   (iii) Drying the ball milled reaction mixture (sample) in an         oven at about 120° C.     -   (iv) Pelletizing the sample and heating at 1450° C. for 10 hours         with one intermediate grinding.     -   (v) The XRD pattern of this compound is shown in FIG. 4     -   (vi) Considering the highest possible oxidation states of the         metals used; (Mg—+2, La—+3 and Sn—+4) the chemical formula of         the compound Magnesium lanthanum Stannate is worked out to be         (Mg₂LaSnO_(5.5)),     -   (vii) The variation of dielectric constant and loss factor of         the compound Mg₂LaSnO_(5.5) is shown in FIG. 5 and FIG. 6. This         clearly shows that the compound is suitable for use as         electronic ceramic material for all applications where         dielectric constant and loss factor play an important role. E.g.         as substrate for superconductors.     -   (viii) The compound does not show any phase transition on         heating up to 1300° C.

EXAMPLE-3 Magnesium Dysprosium Antimonate (Mg₂DySbO₆)

Magnesium Dysprosium Antimonate (Mg₂DySbO₆), for example, is obtained by;

-   -   (i) Taking four gram molecular weight of Magnesium Carbonate         (MgCO₃), one gram molecular weight of dysprosium oxide (Dy₂O₃),         and one gram molecular weight of antimony pentoxide (Sb₂O₅)     -   (ii) Mixing these three reactants by ball milling the mixture         for 18 hours using water as the wetting medium.     -   (iii) Drying the ball milled reaction mixture (sample) in an         oven at about 120° C.     -   (iv) Pelletizing the sample and heating at 1550° C. for 10 hours         with one intermediate grinding.     -   (v) The XRD pattern of this compound is shown in FIG. 7     -   (vi) Considering the highest possible oxidation states of the         metals used, (Mg—+2, Dy—+3 and Sb—+5) the chemical formula of         the compound Magnesium Dysprosium Antimonate is worked out to be         (Mg₂DySbO₆).     -   (vii) The variation of dielectric constant and loss factor of         the compound Mg₂DySbO₆ is shown in FIG. 8 and FIG. 9. This         clearly shows that the compound is suitable for use in all         electronic ceramic 

1. novel compounds of the general formula Mg₂MM′O_(6+x) where M=Y, La or a rare earth metal, M′=Sn, Sb, Zr and Ta, 0.5<x<0.5 having pyrochlore structure, wherein minor variations in the compositions up to 8%, in any of the metal ions is tolerated for the formation of the required phase.
 2. novel compounds as claimed in claim 1, of the formula Mg₂SmTaO₆ as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 3. novel compounds as claimed in claim 1, of the formula Mg₂NdTaO₆ as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 4. novel compounds as claimed in claim 1, of the formula Mg₂DyTaO₆ as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 5. novel compounds as claimed in claim 1, of the formula Mg₂PrTaO₆ as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 6. novel compounds as claimed in claim 1, of the formula Mg₂GdTaO₆ as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 7. novel compounds as claimed in claim 1, of the formula Mg₂EuTaO₆ as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 8. novel compounds as claimed in claim 1, of the formula Mg₂LaTaO₆ as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 9. novel compounds as claimed in claim 1, of the formula Mg₂DySbO₆ as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 10. novel compounds as claimed in claim 1, of the formula Mg₂SmZrO_(5.5) as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 11. novel compounds as claimed in claim 1, of the formula Mg₂NdZrO_(5.5) as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 12. novel compounds as claimed in claim 1, of the formula Mg₂DyZrO_(5.5) as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 13. novel compounds as claimed in claim 1, of the formula Mg₂LaSnO_(5.5) as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 14. novel compounds as claimed in claim 1, of the formula Mg₂GdZrO_(5.5) as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 15. novel compounds as claimed in claim 1, of the formula Mg₂EuZrO_(5.5) as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 16. novel compounds as claimed in claim 1, of the formula Mg₂LaZrO_(5.5) as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 17. novel compounds as claimed in claim. 1, of the formula Mg₂PrZrO_(5.5) as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 18. A process for the preparation of the novel class of compounds as claimed in claim 1 to 17, which comprises: (i) Mixing the compounds of magnesium, M and M′ (where M=Y, La or a rare earth metal, M′=Sn, Sb, Zr and Ta) in such a way as to get the molar ratio of Mg:M:M′ as 2:1:1 required for the formation of the compounds of the general formula Mg₂MM′O_(6+x), wherein minor variations in the compositions up to 8% in any of metal ion is tolerated for the formation of the required phase; (ii) the mixture obtained in step 18(i) is ball milled or mixed with a wetting medium: (iii) the resultant ball milled slurry obtained is dried to remove the liquid and obtain dry powder; (iv) Heating the resultant mixture to a temperature in the range 1000-1600° C. as required for different duration ranging from 3 hour to 50 hours, either in a single step or by taking out the reactant after few hours of heating, checking for phase formation and heating it again after grinding if necessary, upto a maximum of 5 intermediate grindings may be required.
 19. A process as claimed in claim 18, wherein the compounds employed in step 18(i) are selected from their oxides, carbonates chlorides, alkoxides, nitrates, sulfates etc. and preferably the salts used are selected from oxides or carbonate.
 20. A process as claimed in claim 2, wherein the wetting medium used in step 18(ii) is selected from water, alcohol, acetone or any other organic solvent.
 21. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂SmTaO₆ as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 22. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂NdTaO₆ as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 23. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂DyTaO₆ as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 24. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂PrTaO₆ as nanoparticles, having pyrochlore structure wherein minor variation in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 25. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂GdTaO₆ as nanoparticles, having pyrochlore structure wherein minor variations in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 26. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂EuTaO₆ as nanoparticles, having pyrochlore structure wherein minor variations in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 27. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂LaTaO₆, as nanoparticles, having pyrochlore structure wherein minor variations in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 28. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂DySbO₆ as nanoparticles, having pyrochlore structure, wherein minor variations in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 29. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂SmZrO_(5.5) as nanoparticles, having pyrochlore structure, wherein minor variations in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 30. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂NdZrO_(5.5) as nanoparticles, having pyrochlore structure, wherein minor variations in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 31. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂DyZrO_(5.5) as nanoparticles, having pyrochlore structure, wherein minor variations in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 32. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂LaSnO_(5.5) as nanoparticles, having pyrochlore structure, wherein minor variations in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 33. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂GdZrO_(5.5) as nanoparticles, having pyrochlore structure, wherein minor variations in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 34. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂EuZrO_(5.5) as nanoparticles, having pyrochlore structure, wherein minor variations in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 35. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂LaZrO_(5.5) as nanoparticles, having pyrochlore structure, wherein minor variations in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase.
 36. A process as claimed in claim 18 for the preparation of a novel compounds of the formula Mg₂PrZrO_(5.5) as nanoparticles, having pyrochlore structure, wherein minor variations in the compositions upto 8% in any of the metal ions is tolerated for the formation of the phase. 